Effect of thermocycling on the mechanical properties, inorganic particle release and low temperature degradation of glazed high translucent monolithic 3Y-TZP dental restorations.

The influence of thermocycling on the surface deterioration of glazed monolithic high translucent 3Y-TZP dental restorations is still unclear. The purpose of this study therefore was to evaluate low temperature degradation (LTD), elemental release and surface degradation pattern after five years of simulated clinical time. A total of 123 specimens were prepared from second-generation high translucent 3Y-TZP as per ISO 6872:2015 standards (3 mm × 4 mm × 30 mm).

Effect of Two Brands of Glaze Material on the Flexural Strength and Probability of Failure of High Translucent Monolithic Zirconia.

(1) Background: The effect of glazing on the mechanical properties of monolithic high translucent zirconia is not well reported. Therefore, the purpose of this study was to evaluate the effect of glazing on the flexural strength of high translucent zirconia; (2) Methods: Ninety specimens were prepared from second-generation 3Y-TZP high translucent blocks and divided into three groups. Glaze materials were applied on one surface of the specimen and subjected to a four-point bending test and flexural stress and flexural displacement values were derived.