Intercomparison of Indexable Cutting Inserts' Wear Progress and Chip Formation During Machining Hardened Steel AISI 4337 and Austenitic Stainless Steel AISI 316 L.

This article deals with a mutual comparison of indexable cutting inserts of the CNMG 120408 type from two different manufacturers during the machining of hardened steel AISI 4337 and austenitic stainless steel AISI 316 L. The main goal is to analyse the different wear processes depending on the difference in the manufacturer's design and also depending on the properties of the different machined materials. The progress of the wear of the main spine of the tool, the types of wear and the service life of the cutting edge were monitored, with the achievement of the critical value VB = 300 µm being the standard.

Fused Filament Fabrication 3D Printing Parameters Affecting the Translucency of Polylactic Acid Parts.

The effect of 3D printing parameters by Fused Filament Fabrication (FFF) on the translucency of polylactic acid (PLA) parts was investigated. Six different printing parameters were studied: object orientation, layer height, nozzle temperature, fan speed, extrusion multiplier, and printing speed. The commercially available Plasty Mladeč PLA filament and the Original Prusa MK4 3D printer were used for the experiments.

Analyses of Influence on Chromium Coating after Grinding from the View of Final Microstructure and Microhardness in the Surface Layer.

The article deals with the analysis of chromium layer grinding on a steel substrate, where this issue was addressed with regard to the requirements of the manufacturing sector, specifically in the aerospace industry. The experimental samples were chromium-plated and ground under different cutting conditions by the grooving method of grinding. Two types of grinding wheels for grinding were used, grinding wheel based on SG (solgel) a grinding wheel based on SiC.