Mesoporous Zirconium Phenylenesiliconate-phosphonate Hybrids with Ordered Lamellar Nanostructures.

Novel ordered lamellar mesostructure pZrPS-2 was hydrothermally prepared by using zirconium propoxide and 4-(EtO)2OPC6H4Si(OEt)3 (pPPS-E), which was hydrolyzed to organic building units substituted with both siliconate and phosphonate groups, in the presence of Cn TAB and TMAOH. The pZrPS-2 materials were obtained at a Zr/PPS ratio of 2 or higher and the basal spacing was increased by using a longer-chain surfactant (n = 12-18). Removal of the occluded surfactants at 300 °C resulted in retention of the lamellar structure with negligible shrinkage of the interlayer distance.