Mesoporous titania thin film with highly ordered and fully accessible vertical pores and crystalline walls.

We report the preparation of mesoporous titania thin films with the R$\bar 3$m pore structure derived from the Im$\bar 3$m self-assembled ordering of the titania species and an EO(106)PO(70)EO(106) triblock copolymer. The films were spin-cast and then aged at 18 degrees C at a relative humidity of 70 %, which led to the orientation of the Im$\bar 3$m structure with the [111] direction perpendicular to the substrates. The [111] body-diagonal channels became vertical channels upon calcination at 400 degrees C, thus leading to thin films with vertical channels.