Influence of diode laser treatment and casein phosphopeptide-amorphous calcium phosphate paste on eroded root dentin.

Introduction: It is still unclear whether the pretreatment for dentin hypersensitivity can interfere with the adhesive-dentin bonding strength. This study aimed to evaluate the effect of pretreatment with a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste and diode laser on the shear bond strength of the etch-and-rinse adhesive system in the adhesive-dentin interface.

Materials And Methods: Seventy-five bovine root specimens were randomly divided into five experimental groups ( = 15).

Analysis of the Early Stages and Evolution of Dental Enamel Erosion.

The aim of this study was to evaluate by atomic force microscopy (AFM) the early phases and evolution of dental enamel erosion caused by hydrochloric acid exposure, simulating gastroesophageal reflux episodes. Polished bovine enamel slabs (4x4x2 mm) were selected and exposed to 0.1 mL of 0.

A castor oil-containing dental luting agent: effects of cyclic loading and storage time on flexural strength.

Favorable results in the use of castor oil polyurethane (COP) as pulp capping, membrane material, sealer, mouthwash and in bone repair, associated with the fact that Ricinus communis is not derived from petroleum and it is abundant in Brazil, encourage researches in the development of luting agents. Objectives This study compared the flexural strength (FS) of a castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate (COP10) with RelyX ARC (RX) after mechanical cycling (MC) and distilled water storage. Material and Methods Sixty-four specimens (25x2x2 mm) were fabricated and divided into two groups, COP10 and RX (control).

Effect of pretreatment with an Er:YAG laser and fluoride on the prevention of dental enamel erosion.

The aim of this study was to evaluate the effect of the Er:YAG laser and its association with fluoride (1.23% acidulate phosphate fluoride gel) on the prevention of enamel erosion. Sixty specimens were obtained from bovine enamel (4 × 4 mm), which were ground flat, polished, and randomly divided into five groups according to the preventive treatments: control-fluoride application; L--Er:YAG laser; L+F--laser + fluoride; F+L--fluoride + laser; L/F--laser/fluoride simultaneously.

The use of an Er:YAG laser to remove demineralized dentin and its influence on dentin permeability.

The purpose of this study was to analyze, correlate, and compare the demineralization and permeability of dentin remaining after caries removal with either an Er:YAG laser, a bur, or a curette. Thirty human dentin fragments were immersed in a demineralizing solution for 20 days and were randomly divided into three groups (n = 10) for the removal of the demineralized lesion. The groups were G1-Er:YAG laser (200 mJ/6 Hz; noncontact at 12 mm; spot: 0.

Effect of Nd:YAG laser combined with fluoride on the prevention of primary tooth enamel demineralization.

Most studies dealing with the caries preventive action of Nd:YAG laser have been done in permanent teeth and studies on primary teeth are still lacking. The aim of this study was to evaluate in vitro the effect of Nd:YAG laser combined or not with fluoride sources on the acid resistance of primary tooth enamel after artificial caries induction by assessing longitudinal microhardness and demineralization depth. Sixty enamel blocks obtained from the buccal/lingual surface of exfoliated human primary molars were coated with nail polish/wax, leaving only a 9 mm² area exposed on the outer enamel surface, and randomly assigned to 6 groups (n=10) according to the type of treatment: C-control (no treatment); APF: 1.