Correlation of magnetic and magnetoresistive properties of nanoporous Co/Pd thin multilayers fabricated on anodized TiO templates.

In this study, we consider a technological approach to obtain a high perpendicular magnetic anisotropy of the Co/Pd multilayers deposited on nanoporous TiO templates of different types of surface morphology. It is found that the use of templates with homogeneous and smoothed surface relief, formed on silicon wafers, ensures conservation of perpendicular anisotropy of the deposited films inherent in the continuous multilayers. Also, their magnetic hardening with doubling of the coercive field is observed.

Complex magnetic ordering in nanoporous [Co/Pd]-IrMn multilayers with perpendicular magnetic anisotropy and its impact on magnetization reversal and magnetoresistance.

We have systematically investigated the magnetization reversal characteristics and magnetoresistance of continuous and nanoporous [Co/Pd]-IrMn multilayered thin films with perpendicular magnetic anisotropy at different temperatures (4-300 K). For their nanostructuring, porosity was induced by means of deposition onto templates of anodized titania with small (∼30 nm in diameter) homogeneously distributed pores. The magnetization reversal and magnetoresistance of the porous films were found to be closely related to the splitting of the ferromagnetic material into regions with different magnetic properties, in correlation with the complex morphology of the porous system.