Disruption of extended defects in solid oxide fuel cell anodes for methane oxidation.

Point defects largely govern the electrochemical properties of oxides: at low defect concentrations, conductivity increases with concentration; however, at higher concentrations, defect-defect interactions start to dominate. Thus, in searching for electrochemically active materials for fuel cell anodes, high defect concentration is generally avoided. Here we describe an oxide anode formed from lanthanum-substituted strontium titanate (La-SrTiO3) in which we control the oxygen stoichiometry in order to break down the extended defect intergrowth regions and create phases with considerable disordered oxygen defects.