Repair of surgical bone defects grafted with hydroxylapatite + β-TCP and irradiated with λ=850 nm LED light.

The treatment of bone loss due to different etiologic factors is difficult and many techniques aim to improve the repair, including a wide range of biomaterials and recently, photobioengineering. This work aimed to assess by histological analysis the repair of bone defects grafted with biphasic synthetic micro-granular HA + β-TCP associated with LED phototherapy. Forty rats were divided into 4 groups (Clot, LED, Biomaterial and LED + Biomaterial) each subdivided into 2 subgroups according to the time of animal death (15 and 30 days).

Raman spectroscopic study of the repair of surgical bone defects grafted or not with biphasic synthetic micro-granular HA + β-calcium triphosphate irradiated or not with λ850 nm LED light.

The handling of bone losses due to different etiologic factors is difficult and many techniques are aim to improve repair, including a wide range of biomaterials and, recently, photobioengineering. This work aimed to assess, through Raman spectroscopy, the level of bone mineralization using the intensities of the Raman peaks of both inorganic (~960, ~1,070, and 1,077 cm(-1)) and organic (~1,454 and ~1,666 cm(-1)) contents of bone tissue. Forty rats were divided into four groups each subdivided into two subgroups according to the time of sacrifice (15 and 30 days).

Raman ratios on the repair of grafted surgical bone defects irradiated or not with laser (λ780 nm) or LED (λ850 nm).

This work aimed to assess biochemical changes associated to mineralization and remodeling of bone defects filled with Hydroxyapatite+Beta-Beta-tricalcium phosphate irradiated or not with 2 light sources. Ratios of intensities, band position and bandwidth of selected Raman peaks of collagen and apatites were used. Sixty male Wistar rats were divided into 6 groups subdivided into 2 subgroups (15th and 30th days).

Influence of the λ780nm laser light on the repair of surgical bone defects grafted or not with biphasic synthetic micro-granular hydroxylapatite+Beta-Calcium triphosphate.

The treatment of bone loss due to different etiologic factors is difficult and many techniques aim to improve repair, including a wide range of biomaterials and, recently, photobioengineering. This work aimed to assess, through histological analysis The aim of this study was to assess, by light microscopy, the repair of bone defects grafted or not with biphasic synthetic micro-granular Calcium hydroxyapatite (HA)+Beta-TCP associated or not with Laser phototherapy - LPT (λ780nm). Forty rats were divided into 4 groups each subdivided into 2 subgroups according to the time of sacrifice (15 and 30days).

Raman study of the repair of surgical bone defects grafted with biphasic synthetic microgranular HA + β-calcium triphosphate and irradiated or not with λ780 nm laser.

The treatment of bone loss due to different etiologic factors is difficult, and many techniques aim to improve repair, including a wide range of biomaterials and, recently, photobioengineering. This work aimed to assess, through Raman spectroscopy, the level of bone mineralization using the intensities of the Raman peaks of both inorganic (∼ 960, ∼ 1,070, and ∼ 1,077 cm(-1)) and organic (∼ 1,454 and ∼ 1,666 cm(-1)) contents of bone tissue. Forty rats were divided into four groups each subdivided into two subgroups according to the time of killing (15 and 30 days).