Temperature-induced reversible morphological changes of polystyrene-block-poly(ethylene oxide) micelles in solution.

Temperature-induced reversible morphological changes of polystyrene-block-poly(ethylene oxide) micelles with degrees of polymerization of 962 for the PS and 227 for the PEO blocks (PS962-b-PEO227) in N,N-dimethylformamide (DMF)/water, in which water is a selective solvent for the PEO block, were observed. For a system with 0.2 wt % copolymer concentration and 4.

Phase behaviors and supra-molecular structures of a series of symmetrically tapered bisamides.

A series of symmetrically tapered 1,4-bis[3,4,5-tris(alkan-1-yloxy)benzamido] benzene bisamides (CPhBA, where is the number of carbon atoms in the alkyl chains, = 10, 12 and 16), was synthesized in order to investigate the effect of alkyl chain length on supra-molecular ordered structures induced by hydrogen (H)-bonding and micro-phase separation. These bisamides consist of a rigid aromatic bisamide core with three flexible alkyl chains at each end of the core. Major phase transitions and their origins in CPhBA bisamides were studied with differential scanning calorimetry, one-dimensional (1D) wide angle X-ray diffraction (WAXD), infrared spectroscopy, and solid-state carbon-13 nuclear magnetic resonance experiments.

Onset of tethered chain overcrowding.

We proposed an approach to precisely control the density of tethered chains on solid substrates using PEO-b-PS and PLLA-b-PS. As the crystallization temperature Tx increased, the PEO or PLLA lamellar crystal thickness d(L) increased as well as the reduced tethering density sigma; of the PS chains. The onset of tethered PS chains overcrowding in solution occurs at sigma(*) approximately 3.