Compositional and Interfacial Modification of Cu2 ZnSn(S,Se)4 Thin-Film Solar Cells Prepared by Electrochemical Deposition.

A highly efficient Cu2 ZnSn(S,Se)4 (CZTSSe)-based thin-film solar cell (9.9%) was prepared using an electrochemical deposition method followed by thermal annealing. The Cu-Zn-Sn alloy films was grown on a Mo-coated glass substrate using a one-pot electrochemical deposition process, and the metallic precursor films was annealed under a mixed atmosphere of S and Se to form CZTSSe thin films with bandgap energies ranging from 1.

Highly efficient copper-zinc-tin-selenide (CZTSe) solar cells by electrodeposition.

Highly efficient copper-zinc-tin-selenide (Cu2ZnSnSe4 ; CZTSe) thin-film solar cells are prepared via the electrodepostion technique. A metallic alloy precursor (CZT) film with a Cu-poor, Zn-rich composition is directly deposited from a single aqueous bath under a constant current, and the precursor film is converted to CZTSe by annealing under a Se atmosphere at temperatures ranging from 400 °C to 600 °C. The crystallization of CZTSe starts at 400 °C and is completed at 500 °C, while crystal growth continues at higher temperatures.