Structural Studies and Thermal Analysis in the CsMoO-PbMoO System with Elucidation of β-CsPb(MoO).

The quaternary compound CsPb(MoO) was synthesized and its structure was characterized using X-ray and neutron diffraction from 298 to 773 K, while thermal expansion was studied from 298 to 723 K. The crystal structure of the high-temperature phase β-CsPb(MoO) was elucidated, and it was found to crystallize in the space group 3̅ (No. 166), i.

In situ high-temperature EXAFS measurements on radioactive and air-sensitive molten salt materials.

The development at the Delft University of Technology (TU Delft, The Netherlands) of an experimental set-up dedicated to high-temperature in situ EXAFS measurements of radioactive, air-sensitive and corrosive fluoride salts is reported. A detailed description of the sample containment cell, of the furnace design, and of the measurement geometry allowing simultaneous transmission and fluorescence measurements is given herein. The performance of the equipment is tested with the room-temperature measurement of thorium tetrafluoride, and the Th-F and Th-Th bond distances obtained by fitting of the EXAFS data are compared with the ones extracted from a refinement of neutron diffraction data collected at the PEARL beamline at TU Delft.