Influence of Post-Heat Treatment on Corrosion Behaviour of Additively Manufactured CuSn10 by Laser Powder Bed Fusion.

This study investigates the influence of heat treatments on the corrosion behaviour of CuSn10 tin bronze, additively manufactured using Laser Powder Bed Fusion (LPBF). LPBF enables the creation of finely structured, anisotropic microstructures, whose corrosion behaviour is not yet well understood. After production, specimens were heat-treated at 320 °C, 650 °C, and in a two-stage treatment at 800 °C and 400 °C, followed by hardness and microstructure analysis.

Corrosion Resistance of 316L/CuSn10 Multi-Material Manufactured by Powder Bed Fusion.

Research and industry are calling for additively manufactured multi-materials, as these are expected to create more efficient components, but there is a lack of information on corrosion resistance, especially since there is a risk of bimetallic corrosion with two metallic components. In this study, the corrosion behaviour of a multi-material made of 316L and CuSn10 is investigated before and after a stress relief annealing using linear sweep voltammetry. For this purpose, a compromise had to be found in the heat treatment parameters in order to be able to treat both materials together.

V2AlC, V4AlC3-x (x approximately 0.31), and V12Al3C8: synthesis, crystal growth, structure, and superstructure.

Single crystals of V2AlC and the new carbides V4AlC3-x and V12Al3C8 were synthesized from metallic melts. V2AlC was formed with an excess of Al, while V4AlC3-x (x approximately 0.31) and V12Al3C8 require the addition of cobalt to the melt.

Ta3AlC2 and Ta4AlC3--single-crystal investigations of two new ternary carbides of tantalum synthesized by the molten metal technique.

Single crystals of the new ternary carbides Ta4AlC3 and Ta3AlC2 were synthesized from molten aluminum and characterized XRD, EDX, and WDX measurements. Crystal structures were refined for the first time on the basis of single-crystal data. Both compounds crystallize in a hexagonal structure with space group P63/mmc and Z = 2.