Mechanical behavior of yttria-stabilized tetragonal zirconia polycrystalline ceramic after different zirconia surface treatments.

This study investigated the effects of different zirconia surface conditioning methods on the biaxial flexure strength, surface characteristics and fractographic analysis of a Y-TZP ceramic. Disc-shaped specimens were manufactured according to ISO 6872-2008 for biaxial flexure strength testing, and then randomly assigned into seven groups (n=30). Control (CTRL): without treatment; Tribochemical silica coating (TBS): specimens were sandblasted with silica-coated aluminum oxide particles (CoJet-Sand) for 10s; Silica nanofilm (SNF): specimens were silica coated with a 5nm SiO nanofilm; and four protocols of low-fusing porcelain glaze (GLZ): etching with 10% hydrofluoric acid gel (HF) for 1min (GLZ), 5min (GLZ), 10min (GLZ) and 15min (GLZ).

Tribochemical Glass Ceramic Coating as a New Approach for Resin Adhesion to Zirconia.

Purpose: To investigate the effects of a novel tribochemical silica coating technique with powders made from feldspathic ceramic and leucite-based ceramic on the bond strength of zirconia to resin cement before and after aging.

Materials And Methods: Zirconia blocks were divided into 3 groups according to the material used for airborne-particle abrasion: 1) SP (control): silica-coated alumina particles; 2) FP: feldspathic ceramic powder; 3) LP: leucite glass-ceramic powder. After silanization, composite resin cylinders were cemented on the zirconia surface using a dual-curing resin cement.

Adhesion to Y-TZP ceramic: study of silica nanofilm coating on the surface of Y-TZP.

This study evaluated the influence of silica-based film coatings on the surface of yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP), in particular on the durability of the bond strength between the ceramic and resin cement. Eighty Y-TZP (In-Ceram YZ, Vita) blocks (4 × 4 × 3 mm) were obtained and divided into four groups according to the surface treatments (n = 20): tribochemical silica coating (TBS; Cojet, 3M/ESPE), 5 nm SiO2 nanofilm and silanization (F-5), 500 nm SiO2 nanofilm and silanization (F-500), and 500 nm SiO2 nanofilm + hydrofluoric-acid-etching + silanization (F-500HF). Specimens of composite resin (3.