HRTEM observation of bonding interface between Ce-TZP/Al2O3 nanocomposite and porcelain.

The surface of a ceria-stabilized tetragonal zirconia polycrystal (Ce-TZP/Al2O3) nanocomposite was sandblasted by alumina particles and veneered with feldspathic porcelain via a conventional condensation method. The part of each specimen containing the interface layer was sliced to ultrathin sections with an argon ion slicer, and these sliced sections were observed using high-resolution transmission electron microscopy (HRTEM). For both interfaces, Ce-TZP/porcelain and Al2O3/porcelain, no transition layers due to abrupt changes in atomic distributions were observed.

Contamination of dental zirconia before final firing: effects on mechanical properties.

Plate-like specimens were prepared, using a diamond saw, from Cercon -a pre-sintered yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) block. These specimens were treated with 10 kinds of dental materials which acted as contaminants, and then sintered at 1,350°C or 1,450°C. After the final firing, specimens were subjected to a three-point flexural test and Vickers hardness test.

Surface damages of zirconia by Nd:YAG dental laser irradiation.

The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (Ce-TZP/Al₂O₃ nanocomposite) were irradiated by Nd:YAG dental laser. The specimens were characterized using scanning electron microscopy, X-ray diffractometry, and wavelength dispersive X-ray spectroscopy.