A Novel Temperature-Dependent Hydrogel Emulsion with Sol/Gel Reversible Phase Transition Behavior Based on Polystyrene-co-poly(N-isopropylacrylamide)/Poly(N-isopropylacrylamide) Core-Shell Nanoparticle.

As a kind of temperature-responsive hydrogel, polystyrene-co-poly(N-isopropylacrylamide)/poly(N-isopropylacrylamide) (PS-co-PNIPAM/PNIPAM) core-shell nanoparticles prepared by two-step copolymerization are widely studied and used because of their specific structures and properties. Unlike most reports about the steady stability of PS-co-PNIPAM/PNIPAM core-shell nanoparticle hydrogel emulsion, in this work, the PS-co-PNIPAM/PNIPAM core-shell nanoparticle hydrogel emulsion (symbolized as PS/PNIPAM hydrogel emulsion), which is prepared after the second step of synthesis and without washing out a large number of PNIPAM polymer segments, shows a reversible temperature-dependent sol-gel transition characteristic during the temperature range of 34-80 °C. The PS/PNIPAM hydrogel emulsion is a normal solution at room temperature, and it changes from a sol to a gel statue when the temperature approaches up to low critical solution temperature (LCST).

Blocking of checkpoint receptor PD-L1 aggravates osteoarthritis in macrophage-dependent manner in the mice model.

As a chronic degenerative joint disease, osteoarthritis is among the most common diseases all over the world. In osteoarthritis, inflammation plays an important role in the generation of joint symptoms and the development of disease. When the programmed cell death-1 (PD-1)/programmed death-ligand 1 (PD-L1) immune checkpoint is blocked, the antitumor immunity will be enhanced.