The Effect of Boron (B) and Copper (Cu) on the Microstructure and Graphite Morphology of Spheroidal Graphite Cast Iron.

This study examines the impacts of copper and boron in parts per million (ppm) on the microstructure and mechanical properties of spheroidal graphite cast iron (SCI). Boron's inclusion increases the ferrite content whereas copper augments the stability of pearlite. The interaction between the two significantly influences the ferrite content.

Prediction of Extrusion Machine Stem Fatigue Life Using Structural and Fatigue Analysis.

In this study, the characteristics of the SKD61 material used for the stem of an extruder were analyzed through structural analysis, tensile testing, and fatigue testing. The extruder works by pushing a cylindrical billet into a die with a stem to reduce its cross-sectional area and increase its length, and it is currently used to extrude complex and diverse shapes of products in the field of plastic deformation processes. Finite element analysis was used to determine the maximum stress on the stem, which was found to be 1152 MPa, lower than the yield strength of 1325 MPa obtained from tensile testing.

Revealing the enhanced structural recovery and gelation mechanisms of cation-induced cellulose nanofibrils composite hydrogels.

In this study, we fabricate physically dual-crosslinked cellulose-based hydrogels by varying coordination bonding effects with the addition of either divalent or trivalent metal cations. The first crosslinked network is created by metal-carboxylate coordination bonds between the cellulose nanofibrils that have abundant carboxyl groups and the metal cations. The second crosslinked network is formed by the reaction of tetra-functional borate ion complex and the hydroxyl groups in polyvinyl alcohol.

Hydration and oxidation kinetics of a proton conductor oxide, SrCe(0.95)Yb(0.05)O(2.975).

The oxidation and hydration kinetics of a proton conductor oxide, SrCe(0.95)Yb(0.05)O(2.