Initiation and Suppression of Crack Propagation during Magnesium Alloy Rolling.

The conventional rolling of magnesium alloy with a single pass and large reduction will cause severe edge cracking. The sheet without cracks can be achieved by limited width rolling. The microstructure evolution of the sheet with cracks after conventional rolling and the sheet without cracks after limited width rolling is explored, and an effective mechanism for solving edge cracks is proposed.