Charged Impurity Scattering and Electron-Electron Interactions in Large-Area Hydrogen Intercalated Bilayer Graphene.

Intercalation is a promising technique to modify the structural and electronic properties of 2D materials on the wafer scale for future electronic device applications. Yet, few reports to date demonstrate 2D intercalation as a viable technique on this scale. Spurred by recent demonstrations of mm-scale sensors, we use hydrogen intercalated quasi-freestanding bilayer graphene (hQBG) grown on 6H-SiC(0001), to understand the electronic properties of a large-area (16 mm) device.

Large-Area Intercalated Two-Dimensional Pb/Graphene Heterostructure as a Platform for Generating Spin-Orbit Torque.

A scalable platform to synthesize ultrathin heavy metals may enable high-efficiency charge-to-spin conversion for next-generation spintronics. Here, we report the synthesis of air-stable, epitaxially registered monolayer Pb underneath graphene on SiC (0001) by confinement heteroepitaxy (CHet). Diffraction, spectroscopy, and microscopy reveal that CHet-based Pb intercalation predominantly exhibits a mottled hexagonal superstructure due to an ordered network of Frenkel-Kontorova-like domain walls.

Oxidation of Monolayer WS in Ambient Is a Photoinduced Process.

We have studied the ambient air oxidation of chemical vapor deposition (CVD) grown monolayers of the semiconducting transition metal dichalcogenide (S-TMD) WS using optical microscopy, laser scanning confocal microscopy (LSCM), photoluminescence (PL) spectroscopy, and atomic force microscopy (AFM). Monolayer WS exposed to ambient conditions in the presence of light (typical laboratory ambient light for weeks or typical PL spectroscopy map) exhibits damage due to oxidation which can be detected with the LSCM and AFM, though may not be evident in conventional optical microscopy due to poorer contrast and resolution. Additionally, this oxidation was not random and was correlated with "high-symmetry" high intensity edges and red-shifted areas in the PL spectroscopy map, areas thought to contain a higher concentration of sulfur vacancies.

Ambient Protection of Few-Layer Black Phosphorus via Sequestration of Reactive Oxygen Species.

Few-layer black phosphorous (BP) has emerged as a promising candidate for next-generation nanophotonic and nanoelectronic devices. However, rapid ambient degradation of mechanically exfoliated BP poses challenges in its practical deployment in scalable devices. To date, the strategies employed to protect BP have relied upon preventing its exposure to atmospheric conditions.