Pretreatment of rice straw using an extrusion/extraction process at bench-scale for producing cellulosic ethanol.

A combination of a twin-screw extrusion and an acid-catalyzed hot water extraction process performed at a bench-scale was used to prepare high monomeric xylose hydrolysate for cellulosic production. The influences of the screw speed (30-150 rpm), barrel temperature (80-160 °C) and corresponding specific mechanical energy of the extruder on the structural properties of the pretreated rice straw, sugar concentration and conversion were investigated. The optimal condition for the extrusion step was determined to be 40 rpm with 3% H2SO4 at 120 °C; the optimal condition for the extraction step was determined to be 130 °C for 20 min.