The Effect of Nitriding Temperature of AISI 316L Steel on Sub-Zero Corrosion Resistance in CHOH.

In this paper, glow nitriding processes at cathode potential are used at various temperatures to investigate how they affect the corrosion resistance of 316L steel in ethanol at temperatures of 22 °C and -30 °C. Lowering the test temperature reduces the corrosion rate of the nitrided layers. Conversely, glow nitriding at 450 °C improves the corrosion resistance of the tested steel.

Comparison Study of PVD Coatings: TiN/AlTiN, TiN and TiAlSiN Used in Wood Machining.

In this paper, we analyze the possibilities of the protection of tools for wood machining with PVD (Physical Vapor Deposition) hard coatings. The nanolayered TiN/AlTiN coating, nanocomposite TiAlSiN coatings, and single layer TiN coating were analyzed in order to use them for protection of tools for wood machining. Both nanostructured coatings were deposited in an industrial magnetron sputtering system on the cutting blades made of sintered carbide WC-Co, while TiN single layer coating was deposited by evaporation using thermionic arc.

Influence of Different Types of Cemented Carbide Blades and Coating Thickness on Structure and Properties of TiN/AlTiN and TiAlN/a-C:N Coatings Deposited by PVD Techniques for Machining of Wood-Based Materials.

The influence of different types of cemented carbide blades and thickness of TiAlN/a-C:N and TiN/AlTiN protective coatings used in the wood industry on cutting performance has been studied. Three types of WC-Co cemented carbide blades with different cobalt content were used in the study. The thicknesses of both types of coatings were ~2 and ~5 µm.