Properties and Curing Kinetics of a Processable Binary Benzoxazine Blend.

A benzoxazine system is presented combining liquid cardanol-based benzoxazine (CA-a) and an effective initiator (3,3'-thiodipropionic acid, TDA) to bisphenol A-based benzoxazine (BA-a). The resultant mixture of monomeric precursors shows excellent fluidity and a relatively low peak polymerization temperature of around 200 °C. Moreover, the cured polybenzoxazine displays a high thermal decomposition temperature ( > 330 °C), a moderately high glass transition temperature (∼148 °C), and robust mechanical strength (storage modulus ∼ 2.

Polyphosphates can stabilize but also aggregate colloids.

Phosphates are well known as dispersants for a variety of colloidal particles. Here however we use rheological measurements to show that high molecular weight polyphosphates (PP) can instead act as a flocculant for LAPONITE® clay platelets. The proposed mechanism is bridging of PP between clay particle edges, leading to highly charged clusters forming a Wigner glass.