Mechanical Activation and Cation Site Disorder in MgAlO.

The synthesis and crystallographic site occupancy were investigated for MgAlO with and without mechanical activation of the precursor powders. Heating to 1200 °C or higher resulted in the formation of a single spinel phase regardless of whether the powders were mechanically activated or not. Neutron diffraction analysis was used to determine cation site occupancy and revealed that mechanical activation resulted in a lower degree of cation site inversion compared to the nonactivated materials, which indicated that the powders were closer to thermodynamic equilibrium.