Gold Nanocylinders on Gold Film as a Multi-spectral SERS Substrate.

The surface enhanced Raman scattering (SERS) efficiency of gold nanocylinders deposited on gold thin film is studied. Exploiting the specific plasmonic properties of such substrates, we determine the influence of the nanocylinder diameter and the film thickness on the SERS signal at three different excitation wavelengths (532, 638 and 785 nm). We demonstrate that the highest signal is reached for the highest diameter of 250 nm due to coupling between the nanocylinders and for the lowest thickness (20 nm) as the excited plasmon is created at the interface between the gold and glass substrate.

Spin Coating and Micro-Patterning Optimization of Composite Thin Films Based on PVDF.

We optimize the elaboration of very thin film of poly(vinylidene fluoride) (PVDF) polymer presenting a well-controlled thickness, roughness, and nano-inclusions amount. We focused our effort on the spin coating elaboration technique which is easy to transfer to an industrial process. We show that it is possible to obtain continuous and smooth thin films with mean thicknesses of 90 nm by properly adjusting the concentration and the viscosity of the PVDF solution as well as the spin rate and the substrate temperature of the elaboration process.

Self-organized nanoparticle photolithography for two-dimensional patterning of organic light emitting diodes.

We report a new simple and inexpensive sub-micrometer two dimensional patterning technique. This technique combines a use of a photomask featured with self-organized particles in the micro- to nano-meter size range and a photoresist-covered substrate. The photomask was prepared by depositing monodispersed silicon dioxide (SiO(2))- or polystyrene- spheres on a quartz substrate to form a close-packed pattern.