Fiber Orientation and Concentration in an Injection-Molded Ethylene-Propylene Copolymer Reinforced by Hemp.

This paper characterizes and analyzes the microstructures of injection-molded polypropylene parts reinforced with 20 wt% of hemp fibers in order to understand the process induced variations in thermomechanical properties. In-thickness fiber orientation and fiber content were determined by X-ray tomography along the flow. The fiber content along the flow path was also determined by direct fiber content measurements after matrix dissolution, showing an increase of 2%/100 mm for a 2.