Effect of additives on the compressive strength and setting time of a Portland cement.

Improvements in strength and setting time of Portland cements (PC) are needed to enhance their performance as endodontic and load bearing materials. This study sought to enhance the compressive strength and setting time of a PC by adding one of the following additives: 20% and 30% poly-methylmethacrylate (PMMA), 20% and 30% irregular and spherical amalgam alloys, and 10% CaCl(2). The control consisted of unreinforced PC specimens.

Effect of fluoride therapies on the surface roughness of human enamel exposed to bleaching agents.

Objectives: To evaluate in vitro the effect of fluoride therapies on the surface roughness of human dental enamel exposed to bleaching agents.

Method And Materials: Sixty-six specimens obtained from 33 third molars were centrally cut, mounted on acrylic resin supports, polished, and submitted to baseline surface roughness readings (RaB). Next, the specimens were distributed into 11 groups and exposed to one of the bleaching agents-16% carbamide peroxide (CP) or 35% hydrogen peroxide (HP)-and one of the fluoride therapies-0.

Impact of refrigeration on the surface hardness of hybrid and microfilled composite resins.

This in vitro study evaluated the Knoop hardness of the composite resins Charisma (C) and Durafill VS (D) polymerized in 3 different conditions: at room temperature (A) (23 +/- 1 degrees C); refrigerated at 4 +/- 1 degrees C and immediately photo-activated after removal from the refrigerator (0); and, refrigerated at 4 +/- 1 degrees C and photo-activated after a bench time of 15 min at room temperature (15). One hundred and twenty specimens (4 mm diameter and 2 mm depth) were made using a stainless steel mold and following manufacturer's instructions. All specimens were tested immediately after polymerization (I) and after 7 days of water storage in the dark at room temperature (7d).

Fluorescence intensity of resin composites and dental tissues before and after accelerated aging: a comparative study.

This study quantitatively evaluated the fluorescence intensity of resin composites with different opacities and translucencies and determined changes in fluorescence after accelerated aging, using human enamel and dentin as controls. Six microhybrid and nanofilled composites, each in three different shades, were tested. Ten sound human incisors were used to obtain enamel and dentin specimens separately.

Three different methods to evaluate microleakage of packable composites in Class II restorations.

This in vitro study compared three different methods to evaluate detectable levels of microleakage in Class II restorations placed with five commercially available packable resin composites: Alert, Glacier, Pyramid, Solitaire 2 and SureFil. A flowable resin composite, Flow-It, was used to line all packable composites. The hybrid resin composite Z100 was also included.

Influence of curing tip distance on resin composite Knoop hardness number, using three different light curing units.

This in vitro study evaluated the influence of curing tip distance on the Knoop Hardness Number (KHN) of a resin composite when using three different light curing units: (1) a halogen light (XL 1500 curing unit-3M), (2) a "softstart-polymerization" (Elipar Trilight curing in an exponential mode-ESPE) and (3) a PAC (Apolo 95E curing unit-DMD). The resin composite, Filtek Z250 (3M), was cured by these curing units at three light-tip distances from the resin composite: 0 mm, 6 mm and 12 mm. The resin composite specimens were flattened to their middle portion and submitted to 18 KHN measurements perspecimen.