Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition.

The corrosion behavior of duplex Ni-P coatings deposited on AZ91 magnesium alloy was studied. The electroless deposition process of duplex Ni-P coating consisted in the preparation of low-phosphorus Ni-P coating (5.7 wt.

Buccal adhesive films with moisturizer- the next level for dry mouth syndrome?

This study was undertaken to prepare films by solvent evaporation method comprising well-known polymers in order to investigate their potential for buccal suitability. Mucoadhesive films were manufactured using different polymers such as ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl methylcellulose as well as carboxymethyl cellulose. Buccal films were evaluated in regards of mucoadhesiveness, swelling and physico-chemical properties.

Silver Nanoparticles Stabilised by Cationic Gemini Surfactants with Variable Spacer Length.

The present study is focused on the synthesis and investigation of the physicochemical and biological properties of silver nanoparticles stabilized with a series of cationic gemini surfactants having a polymethylene spacer of variable length. UV-VIS spectroscopy, dynamic light scattering, scanning electron microscopy and zeta potential measurements were applied to provide physicochemical characterization of the silver nanoparticles. The mean size values of the nanoparticles were found to be in the 50 to 115 nm range.

Comparison of Electrochemical Methods for the Evaluation of Cast AZ91 Magnesium Alloy.

Linear polarization is a potentiodynamic method used for electrochemical characterization of materials. Obtained values of corrosion potential and corrosion current density offer information about material behavior in corrosion environments from the thermodynamic and kinetic points of view, respectively. The present study offers a comparison of applications of the linear polarization method (from -100 mV to +200 mV vs.

Some Issues of Shrinkage-Reducing Admixtures Application in Alkali-Activated Slag Systems.

Significant drying shrinkage is one of the main limitations for the wider utilization of alkali-activated slag (AAS). Few previous works revealed that it is possible to reduce AAS drying shrinkage by the use of shrinkage-reducing admixtures (SRAs). However, these studies were mainly focused on SRA based on polypropylene glycol, while as it is shown in this paper, the behavior of SRA based on 2-methyl-2,4-pentanediol can be significantly different.