Failure and Degradation Mechanisms of Steel Pipelines: Analysis and Development of Effective Preventive Strategies.

The increasing challenges related to the reliability and durability of steel pipeline infrastructure necessitate a detailed understanding of degradation and failure mechanisms. This study focuses on selective corrosion and erosion as critical factors, analyzing their impact on pipeline integrity using advanced methods, including macroscopic analysis, corrosion testing, microscopic examination, tensile strength testing, and finite element method (FEM) modeling. Selective corrosion in the heat-affected zones (HAZs) of longitudinal welds was identified as the dominant degradation mechanism, with pit depths reaching up to 6 mm, leading to tensile strength reductions of 30%.