A facile strategy for synthesizing isosorbide-based polyurethane structural adhesives and core-shell rubber.

A structural adhesive series of biomass-based polyurethane (Biomass-PU) is synthesized using polypropylene glycol (PPG2000), isosorbide-based polyol (RPO300) as polyols, isophorone diisocyanate (IPDI) as an isocyanate and 4-tert-butylphenol (BP) as a capping agent. Three different equivalent ratios of PPG2000/RPO300, 9/1 (Biomass-PU1), 7/3 (Biomass-PU2), and 1/1 (Biomass-PU3), are evaluated to determine the effect of isosorbide-based polyol content on the properties and the optimizing formulation of biomass-PU structure adhesive. The 9/1 ratio of PPG2000/RPO300 substantially leads to the improvement of impact strength by up to 35 MPa, and the PPG2000/RPO300 = 9/1 ratio exhibits better thermal properties and impact strength than those of other ratios.

Synthesis of Room Temperature Curable Polymer Binder Mixed with Polymethyl Methacrylate and Urethane Acrylate for High-Strength and Improved Transparency.

Urethane acrylate (UA) was synthesized from various di-polyols, such as poly(tetrahydrofuran) (PTMG, Mn = 1000), poly(ethylene glycol) (PEG, Mn = 1000), and poly(propylene glycol) (PPG, Mn = 1000), for use as a polymer binder for paint. Polymethyl methacrylate (PMMA) and UA were blended to form an acrylic resin with high transmittance and stress-strain curve. When PMMA was blended with UA, a network structure was formed due to physical entanglement between the two polymers, increasing the mechanical properties.

Metabolism Of C(14)-Glucose By Plerocercoid Of Diphyllobothrium Sp.

1. The glucose uptake rate by plerocercoid of Diphyllobothrium sp. was a mean value of 5.