Facile fabrication of 2-dimensional arrays of sub-10 nm single crystalline Si nanopillars using nanoparticle masks.

A simple procedure for the fabrication of sub-10 nm scale Si nanopillars in a 2-D array using reactive ion etching with 8 nm Co nanoparticles as etch masks is demonstrated. The obtained Si nanopillars are single crystalline tapered pillar structures of 5 nm (top) x 8 nm (bottom) with a density of approximately 4 x 10(10) pillars cm(-2) on the substrate, similar to the density of Co nanoparticles distributed before the ion etching process. The uniform spatial distribution of the Si nanopillars can also be patterned into desired positions.