Rhizopus stolonifer mediated biosynthesis of biocompatible cadmium chalcogenide quantum dots.

We report an efficient method to biosynthesize biocompatible cadmium telluride and cadmium sulphide quantum dots from the fungus Rhizopus stolonifer. The suspension of the quantum dots exhibited purple and greenish-blue luminescence respectively upon UV light illumination. Photoluminescence spectroscopy, X-ray diffraction, and transmission electron microscopy confirms the formation of the quantum dots.

Dynamics in thermo-responsive nanogel crystals undergoing melting.

We report here the dynamics in thermo-responsive poly(N-isopropylacrylamide) (PNIPAM) nanogel crystals undergoing melting/freezing and verify the applicability of the dynamical criterion for melting/freezing proposed by Löwen et al. [Phys. Rev.

Phase behavior of poly(N-isopropylacrylamide) nanogel dispersions: temperature dependent particle size and interactions.

The phase behavior of poly(N-isopropylacrylamide) nanoparticles dispersed in aqueous medium is investigated as a function of temperature using static and dynamic light scattering techniques. The diameter, d of the particles, as determined by dynamic light scattering measurements on dilute dispersion showed a decrease in size from 273 nm at 25 degrees C to 114 nm at 40 degrees C as function of temperature with a sudden collapse of particle volume (volume phase transition) at 32.4 degrees C.

Random hcp and fcc structures in thermoresponsive microgel crystals.

Monodisperse thermoresponsive poly(N-isopropylacrylamide) (PNIPAM) microgel particles having a diameter of 520 nm were synthesized by free-radical precipitation polymerization and centrifuged to obtain a concentrated suspension. The centrifuged mother suspension was made to self-order into a crystalline state by repeated annealing beyond the volume phase transition (VPT) of the particles. We report here the three-dimensional (3D) real space structure, determined using a confocal laser scanning microscope, of PNIPAM microgel crystal samples prepared by two different recrystallized routes: (1) solidifying a shear melted colloidal liquid (referred as as-prepared sample) and (2) slow cooling of a colloidal liquid (referred as recrystallized sample).