Synthesis of Mixed Cu/Ce Oxide Nanoparticles by the Oil-in-Water Microemulsion Reaction Method.

Cerium oxide and mixed Cu/Ce oxide nanoparticles were prepared by the oil-in-water (O/W) microemulsion reaction method in mild conditions. The Cu/Ce molar ratio was varied between 0/100 and 50/50. According to X-ray diffraction (XRD), below 30/70 Cu/Ce molar ratio, the materials presented a single phase consistent with cubic fluorite CeO₂.

Photodegradation of indigo carmine and methylene blue dyes in aqueous solution by SiC-TiO2 catalysts prepared by sol-gel.

Indigo carmine and methylene blue dyes in aqueous solution were photodegraded using SiC-TiO(2) catalysts prepared by sol-gel method. After thermal treatment at 450°C, SiC-TiO(2) catalysts prepared in this work showed the presence of SiC and TiO(2) anatase phase. Those compounds showed specific surface area values around 22-25 m(2)g(-1), and energy band gap values close to 3.

Methylene blue degradation by NaTaO3 sol-gel doped with Sm and La.

In this work, NaTaO(3) compounds doped with 1M% of La and Sm, were prepared by the sol-gel (SG) method and solid state (SS) reaction; and tested as photocatalysts on the degradation of methylene blue (MB) under UV light. The structural characterization by X-ray powder diffraction revealed that the crystallization of the NaTaO(3) phase prepared by the sol-gel method started at 600 degrees C, reaching maximum crystallization at 800 degrees C. It was determined that the presence of Sm and La retard the crystallization of the NaTaO(3) phase.