Enhancement of the Insulation Properties of Poly(2-oxazoline)-co-Polyester Networks by the Addition of Nanofillers.

Copoly(2-nonyl-2-oxazoline)-stat-poly(2-dec-9'enyl-2-oxazoline)s can be crosslinked by the thiol-ene reaction with glycol dimercaptoacetate. The copoly(2-oxazoline)-stat-copolyester is tested as dielectric for high-voltage applications, either as unfilled resin or as composite with nanoscaled fillers of silica, alumina, and hexagonal boron nitride. During AC voltage tests, all materials have an average breakdown strength of 45-50 kV mm .

Effect of Interfacial Polarization and Water Absorption on the Dielectric Properties of Epoxy-Nanocomposites.

Five types of nanofillers, namely, silica, surface-silylated silica, alumina, surface-silylated alumina, and boron nitride, were tested in this study. Nanocomposites composed of an epoxy/amine resin and one of the five types of nanoparticles were tested as dielectrics with a focus on (i) the surface functionalization of the nanoparticles and (ii) the water absorption by the materials. The dispersability of the nanoparticles in the resin correlated with the composition (OH content) of their surfaces.

Crosslinked Poly(2-oxazoline)s as "Green" Materials for Electronic Applications.

Poly(2-nonyl-2-oxazoline)--poly(2-dec-9'-enyl-2-oxazoline) and poly(2-dec-9'-enyl-2-oxazoline) can be synthesized from the cationic ring-opening polymerization of monomers that can be derived from fatty acids from renewable resources. These (co)poly(2-oxazoline)s can be crosslinked with di- and trifunctional mercapto compounds using the UV-induced thiol-ene reaction. The complex permittivity of the corresponding networks increases with the temperature and decreases with the network density.