Strain Field Around Individual Dislocations Controls Failure.

Understanding material failure on a fundamental level is a key aspect in the design of robust structural materials, especially for metals and alloys capable to undergo plastic deformation. In the last decade, significant progress is made in quantifying the stresses associated with failure in both experiments and simulations. Nonetheless, the processes occurring on the most essential level of individual dislocations that govern semi-brittle and ductile fracture are still experimentally not accessible, limiting the failure prediction capabilities.

Deformation Induced Structure and Property Changes in a Nanostructured Multiphase CrMnFeCoNi High-Entropy Alloy.

A nanocrystalline CrMnFeCoNi high-entropy alloy produced using severe plastic deformation using high-pressure torsion was annealed at selected temperatures and times (450 °C for 1 h and 15 h and at 600 °C for 1 h), causing a phase decomposition into a multi-phase structure. The samples were subsequently deformed again by high-pressure torsion to investigate the possibility of tailoring a favorable composite architecture by re-distributing, fragmenting, or partially dissolving the additional intermetallic phases. While the second phase in the 450 °C annealing states had high stability against mechanical mixing, a partial dissolution could be achieved in the samples subjected to 600 °C for 1 h.