The Intermetallic Semiconductor -IrGa: a Material in the State.

The compound IrGa was synthesized by direct reaction of the elements. It is formed as a high-temperature phase in the Ir-Ga system. Single-crystal X-ray diffraction analysis confirms the tetragonal symmetry (space group 4 , No.

In Situ Observation of Electron-Beam-Induced Formation of Nano-Structures in PbTe.

Nano-scaled thermoelectric materials attract significant interest due to their improved physical properties as compared to bulk materials. Well-shaped nanoparticles such as nano-bars and nano-cubes were observed in the known thermoelectric material PbTe. Their extended two-dimensional nano-layer arrangements form directly in situ through electron-beam treatment in the transmission electron microscope.

In Situ Growth and Size Regulation of Single Gold Nanoparticles in Composite Microgels.

Herein, a novel method for the in situ growth of single gold nanoparticles (AuNPs) in microgel (MG) networks is presented. The key feature in this approach is the localization of β-diketone groups capable of both complexation and reduction of aurate ions in the MGs' core, which allows localization of the nucleation and growth of single AuNPs. The MG synthesis is carried out via precipitation polymerization in water with N-vinylcaprolactam as the main monomer and with the two comonomers acetoacetoxyethyl methacrylate (AAEM) and acrylic acid (AAc), where AAEM is mainly located in the MGs' core and AAc in their shell.

Tracking aluminium impurities in single crystals of the heavy-fermion superconductor UBe.

The influence of Al incorporation on the heavy fermion superconductor UBe was investigated to explain the sample dependence of physical properties. Clear evidence for incorporated Al in flux-grown UBe single crystals is presented by results from X-ray diffraction, nuclear magnetic resonance and X-ray spectroscopy. The increase of the lattice parameter and the concomitant change of the superconducting properties are caused by substitution of Be in the compound by 1-2 at.

[Effect of Ultrasmall Gold Nanoparticles on the Murine Native Sperm Chromatin].

The effects of ultrasmall (2-3 nm) gold nanoparticles on native epididymal sperm chromatin of CBAxC57BL/6 hybrid mice and 129/IMG mice with a mutation in the DNA-polymerase iota gene were studied. It is shown that for both mouse strains after sperm incubation in a solution containing Au nanoparticles, at 23, 37 and 60 degrees C for 30 min followed by 1 hour treatment in dithiothreitol solution, a decrease in the number of nuclei with fully decondensed chromatin was observed compared with the control. Though, the manifestation of this effect in the population of 129/IMG mice mature sperm, was weaker.