Evaluation of alumina slurry dispersion by nuclear magnetic resonance relaxation as a comparison to conventional dispersion evaluation methods.

In this paper, we evaluated the particle dispersion degree of alumina slurry containing a dispersant by solvent nuclear magnetic resonance (NMR) relaxation and compared it with conventional dispersion evaluation methods such as viscosity, particle size, and sedimentation height measurements. The dispersion of slurry was evaluated via numerical analysis of the transverse relaxation time (T ). The effect of the changes in different parameters of the experiment in terms of milling time, solid loading, and dispersant amount was investigated by NMR relaxation as well as conventional methods.

Fabrication of Large-Area Molybdenum Disulfide Device Arrays Using Graphene/Ti Contacts.

Two-dimensional (2D) molybdenum disulfide (MoS) is the most mature material in 2D material fields owing to its relatively high mobility and scalability. Such noticeable properties enable it to realize practical electronic and optoelectronic applications. However, contact engineering for large-area MoS films has not yet been established, although contact property is directly associated to the device performance.

Dispersion Optimization of Alumina Slurry with Variation of the Dispersant.

Plate-type alumina ceramics are widely applied as the major components in display and semiconductor manufacturing equipment. These materials are mainly produced by a filter casting method. There have been few studies on the dispersion of these slurries.

Effects of Y₂O₃ Additive on Mechanical and Thermal Properties of Cordierite-Mullite Ceramics.

Cordierite is an alumina-magnesia-silica compound widely used as a thermal shock resistant material due to its high thermal shock resistance, low coefficient of thermal expansion (CTE), low dielectric constant, and good electrical insulation. However, its narrow sintering temperature range and low mechanical strength hinder its application in ceramic heaters. Although mullite shows excellent thermal and chemical stability, heat resistance, and mechanical strength, it has the disadvantages of high sintering temperatures (1600-1700 °C) and poor thermal shock resistance.

Sintering and Microstructure of BaTiO3 Nano Particles Synthesized by Molten Salt Method.

In order to establish thinner dielectric layers in thick film electronic components such as MLCC (Multilayer ceramic capacitor), BaTiO3 nanoparticles have been utilized. However, studies on the synthesis of nanoparticles smaller than 20 nm, the characteristics of the BaTiO3 powder, and the powder's sintering are lacking. Therefore, this paper aims to synthesize BaTiO3 particles smaller than 20 nm by using the molten salt method and evaluate the microstructure and dielectric properties by varying the sintering temperature from 750 degrees C to 1200 degrees C.

Effect of Ca-Al-Si-O common glass on dielectric properties of low-temperature co-fired ceramic materials with different fillers.

High-density integration in single component used for mobile communication is highly demanded with the miniaturization trend in multi-functional light-weighted mobile communication devices. Embedding passive components into multi-layered ceramic chips is also increasingly needed for high integrity. The need for high strength materials to be used in handheld devices has also increased.