In vitro biocompatibility of novel Au-Pt-based metal-ceramic alloys.

The aim of this research was to evaluate the effect of individual metallic elements within experimental Au-Pt-based metal-ceramic alloys on in vitro biocompatibility. A binary Au-10 at.% Pt alloy (AP10) was designed as a parent alloy.

The effect of investment materials on the surface of cast fluorcanasite glasses and glass-ceramics.

Modified fluorcanasite glass-ceramics were produced by controlled two stage heat-treatment of as-cast glasses. Castability was determined using a spiral castability test and the lost-wax method. Specimens were cast into moulds formed from gypsum and phosphate bonded investments to observe their effect on the casting process, surface roughness, surface composition and biocompatibility.

In vitro biocompatibility of fluorcanasite glass-ceramics for bone tissue repair.

Fluorcanasite glass-ceramics were produced by controlled two stage heat-treatment of as-cast glasses. These glasses were modified from stoichiometric fluorcanasite composition by either adding P(2)O(5) or altering the molar ratios of Na(2)O and CaO. Commercial bioactive 45S5 Bioglass(R) was also prepared in-house to evaluate the relative in vitro biocompatibility of fluorcanasite glass-ceramics.

Biocompatibility of glass-ionomer bone cements.

Glass-ionomer cements (GIC) have been extensively used in dentistry for over 30 years. Due to their excellent biocompatibility in dental applications GIC have been formulated for medical applications. The past decade has seen some impressive advances in the development of medical GICs, however these advances have been matched by serious critical problems.

In vitro biocompatibility of a novel Fe2O3 based glass ionomer cement.

Introduction: Since their invention in the late 1960s, glass ionomer cements (GICs) have been used extensively in dentistry but recently they have also been utilised in ear nose and throat (ENT) surgery. Unfortunately, Al3+, a component of conventional ionomer glasses, has been linked to poor bone mineralisation and neurotoxicity.

Objective: The aim of the research was to modify a commercial ionomer glass composition by substituting Al2O3 with Fe2O3.

Devitrification of ionomer glass and its effect on the in vitro biocompatibility of glass-ionomer cements.

The effects of devitrification of an ionomer glass with a molar composition 4.5SiO(2).3Al(2)O(3).