Electrochemical Polymerization of PEDOT-Graphene Oxide-Heparin Composite Coating for Anti-fouling and Anti-clotting of Cardiovascular Stents.

In this study, a novel hemocompatible coating on stainless steel substrates was prepared by electrochemically copolymerizing 3,4-ethylenedioxythiophene (EDOT) with graphene oxide (GO), polystyrene sulfonate (PSS), or heparin (HEP) on SUS316L stainless steel, producing an anti-fouling (anti-protein adsorption and anti-platelet adhesion) surface to avoid the restenosis of blood vessels. The negative charges of GO, PSS, and HEP repel negatively charged proteins and platelets to achieve anti-fouling and anti-clotting. The results show that the anti-fouling capability of the poly(3,4-ethylenedioxythiophene) (PEDOT)/PSS coating is similar to that of the PEDOT/HEP coating.

Hemocompatibility and anti-fouling behavior of multilayer biopolymers immobilized on gold-thiolized drug-eluting cardiovascular stents.

To solve the thrombosis and restenosis problem in cardiovascular stent implantation for cardiovascular artery disease, chondroitin 6-sulfate (ChS) with heparin (HEP) have been used as drug carrier layers and alternatively covalently bonded on gold (Au)-dimercaptosuccinic acid (DMSA)-thiolized cardiovascular metallic (SUS316 L stainless steel, SS) stents. Sirolimus, a model drug, was encapsulated in the ChS-HEP alternative layers. The behavior of the drug in releasing and suppressing the growth of smooth-muscle cells (SMCs) was evaluated with 5-layer CHS-HEP coating on the SS stents.

Core-shell of FePt@SiO2-Au magnetic nanoparticles for rapid SERS detection.

In this study, multifunctional hybrid nanoparticles composed of iron platinum (FePt), silica (SiO2), and gold nanoparticles (AuNPs) had been developed for surface-enhanced Raman scattering (SERS) application. Core-shell structure of SiO2 and FePt nanoparticles (FePt@SiO2) was fabricated through sol-gel process and then immobilized gold nanoparticles onto the surface of FePt@SiO2, which displays huge Raman enhancement effect and magnetic separation capability. The resulting core-shell nanoparticles were subject to evaluation by transmission electron microscopy (TEM), Energy-dispersive X-ray spectroscopy (EDX), zeta potential measurement, and X-ray photoelectron spectroscopy (XPS).