Transition behaviors of γ-β/β in V-, Cr-, Mn-doped TiAl alloys.

The behavior of γ-β/β phase transition in TiAl alloy doped with β stabilizers (V, Cr, Mn) are studied by using the first principles method. It is found that alloying addition as well as anharmonic lattice vibration and disordered atomic occupation contributes to enhance the stability of cubic structure and accordingly introduce the disordered β phase into the high-temperature microstructure. The formation of low-temperature β phase originates from not only the stabilization of cubic structure but also the destabilization of tetragonal structure.