Anisotropic optical transmission of femtosecond laser induced periodic surface nanostructures on indium-tin-oxide films.

Two types of periodic nanostructures, self-organized nanodots and nanolines, were fabricated on the surfaces of indium-tin-oxide (ITO) films using femtosecond laser pulse irradiation. Multiple periodicities (approximately 800 nm and 400 nm) were clearly observed on the ITO films with nanodot and nanoline structures and were identified using two-dimensional Fourier transformation patterns. Both nanostructures show the anisotropic transmission characteristics in the visible range, which are strongly correlated with the geometry and the metallic content of the laser-induced nanostructures.

Superior local conductivity in self-organized nanodots on indium-tin-oxide films induced by femtosecond laser pulses.

Large-area surface ripple structures of indium-tin-oxide films, composed of self-organized nanodots, were induced by femtosecond laser pulses, without scanning. The multi-periodic spacing (~800 nm, ~400 nm and ~200 nm) was observed in the laser-induced ripple of ITO films. The local conductivity of ITO films is significantly higher, by approximately 30 times, than that of the as-deposited ITO films, due to the formation of these nanodots.