Gradient-Modified HfC-SiC Mixed Bi-Interlayers Synthesized under Different TMS Flow Rate Increment for Depositing Diamond Coating onto WC-Co Substrate.

To deposit well-adhered diamond coating, gradient-modified hafnium carbide-silicon carbide (HfC-SiC) mixed bi-interlayers were prepared on cemented carbides (WC-Co) by plasma surface metallurgy technique under the different tetramethylsiline (TMS) flow rate increment. The effects of the TMS flow rate increment on the composition, microstructure, adhesion, and hardness of the bi-interlayers were investigated. Then, the well-adhered bi-interlayer was chosen for the deposition of the diamond coating.

Preparation, Microstructure, Mechanical Properties and Biocompatibility of Ta-Coated 3Y-TZP Ceramic Deposited by a Plasma Surface Alloying Technique.

A Ta coating has been successfully fabricated on the surface of zirconia polycrystals ceramic (3 mol% yttria, 3Y-TZP) by a plasma surface alloying technique. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) results showed that a -Ta coating with a continuous and compact surface morphology which consisted of a deposited layer with a thickness of 390 nm and a diffusion layer with a thickness of 200 nm covered the 3Y-TZP. Due to the effect of inhabitation the t→m transformation by the deposited Ta coating, the biaxial flexural strength caused by the phase transformation during hydrothermal aging is reduced e.