Synthesis of Si nanosheets by a chemical vapor deposition process and their blue emissions.

We synthesized free-standing Si nanosheets (NSs) with a thickness of about <2 nm using a chemical vapor deposition process and studied their optical properties. The Si NSs were formed by the formation of frameworks first along six different <110> directions normal to [111], its zone axis, and then by filling the spaces between the frameworks along the <112> directions under high flow rate of processing gas. The Si NSs showed blue emission at 435 nm, and absorbance and photoluminescence (PL) excitation measurements indicate that enhanced direct band transition attributes to the emission.

Observation of red-shifted strong surface plasmon scattering in single Cu nanowires.

Surface plasmon scattering spectra of chemically produced single Cu nanowires were obtained using a total internal reflection microscope. In particular, we have observed a strong surface plasmon peak in the far red and a red-shift of the surface plasmon resonance with increasing nanowire diameter. We believe that the most reasonable origin for the red-shift of comparably large diameter nanowires is the phase retardation effect.