Highly efficient NIR to NIR upconversion of ZnMoO:Tm,Yb phosphors and their application in biological imaging of deep tumors.

ZnMoO:Tm,Yb,K nano-phosphors with intense NIR to NIR (excitation by 980 nm, emission at ∼800 nm) upconversion were synthesized by a facile hydrothermal method. The nanoparticles were of the order of 200-400 nm. The XRD patterns confirmed a single phase triclinic structure despite doping small amounts of RE and alkali ions.

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads.

TiO2 immobilized on SiO2 (TiO2/SiO2) have been prepared by sol-gel method and various ions of transition metals (Cr3+, Co2+ Ni2+, CU2+, and Zn2+) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO2/SiO2 towards phenol degradation under black light irradiation were investigated and compared with undoped TiO2/SiO2. The results showed that the photoresponse of Cu2+ and Zn2+ doped TiO2/SiO2 were larger than undoped TiO2/SiO2, indicating that the photogenerated carriers were separated more efficiently in Cu2+ and Zn2+ doped TiO2/SiO2.

Novel LaBO3 hollow nanospheres of size 34±2 nm templated by polymeric micelles.

Novel lanthanum borate (LaBO(3)) hollow nanospheres of size 34±2 nm have been reported for the first time by soft-template self-assembly process. Poly(styrene-b-acrylic acid-b-ethylene oxide) (PS-PAA-PEO) micelle with core-shell-corona architecture serves as an efficient soft template for fabrication of LaBO(3) hollow particles using sodium borohydride (NaBH(4)) and LaCl(3)⋅7H(2)O as the precursors. In this template, the PS block (core) acts as a template of the void space of hollow particle, the anionic PAA block (shell) serves as reaction field for metal ion interactions, and the PEO block (corona) stabilizes the polymer/lanthana composite particles.

Chemical modification of carbonized wheat and barley straw using HNO3 and the adsorption of Cr(III).

The effects of oxidation using HNO(3) on the properties of the carbonized wheat and barley straw were investigated by measuring different properties such as specific surface area, PZC, total surface acidic groups as well as FTIR and TG-DTA. A small decrease in the specific surface area due to pore blockage was observed after oxidation. After oxidation, the acidity was increased considerably and the point of zero charge shifted from approximately pH 9 to pH 2 in both types of carbon.