Microcontact printing for patterning carbon nanotube/polymer composite films with electrical conductivity.

Patterned carbon nanotube (CNT)/acrylic resin composite films were prepared using microcontact printing (μCP). To prepare ink for μCP, CNTs were dispersed into propylene glycol monomethyl ether acetate (PGMEA) solution in which acrylic resin and a commercially available dispersant (Disperbyk-2001) dissolved. The resulting ink were spin-coated onto poly(dimethylsiloxane) (PDMS) stamps.

Hard and glossy-colored films composed of micropatterned organic dots and electrodeposited honeycomb-shaped nickel walls.

This paper proposes a novel approach for the preparation of colored films with a metallic luster and high hardness. The colored organic films were patterned as microdots by photolithography, and then honeycomb-shaped Ni walls were electrodeposited between the micropatterning. The organic/inorganic composite films showed the hardest grade in a pencil hardness test and high durability in wear resistance tests because the honeycomb-shaped Ni walls protected the colored organic dots.