Photocatalytic antibacterial performance of Sn(4+)-doped TiO(2) thin films on glass substrate.

Pure anatase, nanosized and Sn(4+) ion doped titanium dioxide (TiO(2)) particulates (TiO(2)-Sn(4+)) were synthesized by hydrothermal process. TiO(2)-Sn(4+) was used to coat glass surfaces to investigate the photocatalytic antibacterial effect of Sn(4+) doping to TiO(2) against gram negative Escherichia coli (E. coli) and gram positive Staphylococcus aureus (S.

Photocatalytic degradation of Congo Red by hydrothermally synthesized nanocrystalline TiO2 and identification of degradation products by LC-MS.

Degradation of Congo Red (CR) dye in aqueous solutions was investigated by means of photocatalysis of TiO2 which was hydrothermally synthesized at 200 degrees C in 2 h, in anatase phase with 8 nm crystallite size. Efficiency of TiO2 in photocatalytic degradation under visible irradiation was studied by investigating the effects of amount of TiO2, irradiation time, initial CR concentration and pH. It was found that complete decolorization is achieved within 30 min of irradiation.

Characterization of the hydrothermally synthesized nano-TiO2 crystallite and the photocatalytic degradation of Rhodamine B.

Pure anatase-TiO2 nanoparticles with 8 nm average crystallite size was synthesized hydrothermally at 200 degrees C in 2 h. The structural and physico-chemical properties of nano-TiO2 were determined by powder XRD, FT-IR, BET and SEM analyses. The behavior of anatase nano-TiO2 in catalytic degradation of Rhodamine B (RB) dye in transparent nano-TiO2 sol under UV-light was examined as a function of irradiation power of UV-light, irradiation time, amount of nano-TiO2 and initial RB concentration in the sol.

The production and application of a regenerable filter system for adsorption of some atmospheric contaminants.

In this work, a new filter, used to prevent atmospherical pollution, has been developed. Spherical amorphous shaped silicates (such as KC-Siliperl AF 125 and Aluminium silicate 596 FA) were coated with different materials which were prepared from the hydrolysis-condensation products of organically modified silanes and metal alkoxides. The adsorption capacities of such silicates for different solvents; ethylacetate, toluene, n-hexane and cyclohexanone were investigated.