Comparative study of Nd:YAG laser-induced breakdown spectroscopy and transversely excited atmospheric CO2 laser-induced gas plasma spectroscopy on chromated copper arsenate preservative-treated wood.

Taking advantage of the specific characteristics of a transversely excited atmospheric (TEA) CO(2) laser, a sophisticated technique for the analysis of chromated copper arsenate (CCA) in wood samples has been developed. In this study, a CCA-treated wood sample with a dimension of 20 mm × 20 mm and a thickness of 2 mm was attached in contact to a nickel plate (20 mm × 20 mm × 0.15 mm), which functions as a subtarget.

Direct analysis of powder samples using transversely excited atmospheric CO2 laser-induced gas plasma at 1 atm.

A novel method for the direct and sensitive analysis of powder samples has been developed by utilizing the characteristics of a transversely excited atmospheric (TEA) CO(2) laser. In this study, a powder sample was placed in a container and covered by a metal mesh; the metal mesh functions to control the blowing-off of the powder. The container was then perpendicularly attached on a metal surface.

Quantitative deuterium analysis of titanium samples in ultraviolet laser-induced low-pressure helium plasma.

An experimental study of ultraviolet (UV) laser-induced plasma spectroscopy (LIPS) on Ti samples with low-pressure surrounding He gas has been carried out to demonstrate its applicability to quantitative micro-analysis of deuterium impurities in titanium without the spectral interference from the ubiquitous surface water. This was achieved by adopting the optimal experimental condition ascertained in this study, which is specified by 5 mJ laser energy, 10 Torr helium pressure, and 1-50 mus measurement window, which resulted in consistent D emission enhancement and effective elimination of spectral interference from surface water. As a result, a linear calibration line exhibiting a zero intercept was obtained from Ti samples doped with various D impurity concentrations.

Quantitative hydrogen analysis of zircaloy-4 in laser-induced breakdown spectroscopy with ambient helium gas.

This experiment was carried out to address the need for overcoming the difficulties encountered in hydrogen analysis by means of plasma emission spectroscopy in atmospheric ambient gas. The result of this study on zircaloy-4 samples from a nuclear power plant demonstrates the possibility of attaining a very sharp emission line from impure hydrogen with a very low background and practical elimination of spectral contamination of hydrogen emission arising from surface water and water vapor in atmospheric ambient gas. This was achieved by employing ultrapure ambient helium gas as well as the proper defocusing of the laser irradiation and a large number of repeated precleaning laser shots at the same spot of the sample surface.

Quantitative hydrogen analysis of zircaloy-4 using low-pressure laser plasma technique.

It is found in this work that variation of laser power density in low-pressure plasma spectrochemical analysis of hydrogen affects sensitively the hydrogen emission intensity from the unwanted and yet ubiquitous presence of ambient water. A special experimental setup has been devised to allow the simple condition of focusing/defocusing the laser beam on the sample surface. When applied to zircaloy-4 samples prepared with various hydrogen impurity concentrations using low-pressure helium surrounding gas, good-quality hydrogen emission lines of very high signal to background ratios were obtained with high reproducibility under weakly focused or largely defocused laser irradiation.