Study of a hydraulic DCPA/CaO-based cement for dental applications.

A CPC was obtained by mixing calcium hydrogenphosphate (DCPA: CaHPO(4)) and calcium oxide with either water or sodium phosphate (NaP) buffers. Physical and mechanical properties such as compressive strength (CS), initial (I) and final (F) setting times, cohesion time (T(C)), dough time (T(D)), swelling time (T(S)), dimensional and thermal behavior, injectability (t(100%)), antimicrobial properties, setting reaction kinetics, and powder stability over time were investigated by varying different parameters such as liquid-to-powder (L/P) ratio (0.35 to 0.

Antimicrobial activity and tightness of a DCPD-CaO-based hydraulic calcium phosphate cement for root canal filling.

Calcium hydroxide is currently used in dentistry for endodontic treatments where its main advantage is its antibacterial and anti-inflammatory activity. However, it also has some drawbacks such as pulp necrosis, slight solubility, slow and insufficient hardening, and retraction on drying. In consequence, it is used only as temporary material for root canal disinfection.

Study of a hydraulic dicalcium phosphate dihydrate/calcium oxide-based cement for dental applications.

By mixing CaHPO(4) x 2H(2)O (DCPD) and CaO with water or sodium phosphate buffers as liquid phase, a calcium phosphate cement was obtained. Its physical and mechanical properties, such as compressive strength, initial and final setting times, cohesion time, dough time, swelling time, dimensional and thermal behavior, and injectability were investigated by varying different parameters such as liquid to powder (L/P) ratio (0.35-0.