The enhanced shear bond strength of resin cement to zirconia with ordered conical spots through the CO laser process.

In this study, a new shear bonding system was created that uses a CO laser to form a pattern of conical spots on a zirconia prosthesis surface to improve mechanical interlocking. Four types of zirconia substrates were employed, which underwent particle abrasion after being polished, machined, spotted, and spot-particle abraded. The surface roughness of each substrate was measured via scanning electron microscopy and X-ray diffraction (XRD).

Effects of silica sputtering on adhesion between zirconia and composite resin cores.

Radiofrequency magnetron sputtering of silicon was applied onto zirconia surfaces by use of a non-doped Si wafer at 2%, 5%, 8%, and 10% oxygen volumes. Immediately after sputtering, the contact angle was practically 0 for all oxygen volume specimens. In terms of sustainability of the hydrophilicity, however, 5% oxygen volume was found to be optimal.

Promotion of Nickel (Ni) Allergy by Anamnestic Sensitization with a Bacterial Component, Lipopolysaccharide (LPS), in Mice.

Background/objective: Lipopolysaccharides (LPS) promote allergic responses to nickel (Ni) both in the sensitization and elicitation steps. In this study, we examine the effect of pre-sensitization to LPS on the occurrence of Ni allergy using a mouse model.

Method: A 100 mg of LPS was injected into C57BL/6J mice intraperitoneally (ip).

Effects of dental porcelain containing silver nanoparticles on static fatigue.

The purpose of this study was to clarify the effect of silver nanoparticles on the behavior of subcritical crack growth (SCG) in dental porcelains. Prior to occurrence of fast fracture in dental porcelains, SCG occurs and leads to strength degradation over time. SCG in dental porcelains can be characterized by the stress corrosion susceptibility coefficient, n.

Toughening of CAD/CAM all-ceramic crowns by staining slurry.

The ability of staining slurries containing silver and/or potassium compounds to enhance the mechanical properties of a leucite-reinforced glass ceramic (IPS Empress CAD) was investigated by measuring the Vickers hardness, median crack length, toughness, and compressive residual stress of specimens. A staining slurry containing potassium ions was found to increase the toughness of IPS specimens more than a staining slurry containing only silver ions when applied prior to sintering. None of the staining slurries produced any color changes.

Addition of platinum and silver nanoparticles to toughen dental porcelain.

Several studies have investigated toughening porcelain that is layered over a frame or a core. The introduction of residual compressive stress to the surface of porcelain has been shown to be effective to strengthen it. In the present study, nanoparticles of precious metals of silver and platinum (rather than non-precious metals) were used to evaluate if they could increase the fracture resistance of porcelain.