Bond strength of resin-based restorative materials to fast-setting calcium silicate cement using different resin adhesive systems.

This study assessed the bond strength of resin-based restorative materials to fast-setting calcium silicate cement (Aarhus Uinversity, Denmark) when treated with each of two one-bottle universal adhesive systems. The cement surface (N = 256) was treated with a self-priming adhesive and a self-etch phosphate monomer-containing adhesive with and without etching of the cement surface. Specimens then received either resin composite or compomer restorative materials (n = 32).

Validation of a human saliva model for the determination of leachable monomers and other chemicals from dental materials.

This study aimed to prove the validity of a mixture of chemicals, including salts, small organic molecules, mucin, and α-amylase, as saliva surrogate ("artificial saliva") for assessing leakage of methacrylate monomers and other constituents from dental materials. To achieve this, we developed and validated a liquid chromatography-tandem mass spectrometry (LC-MS/MS) method for the quantification of 2-hydroxyethyl methacrylate (HEMA), triethylene glycol dimethacrylate (TEGDMA), diurethane dimethacrylate (UDMA), bisphenol A glycerolate dimethacrylate (BisGMA), diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO), bisphenol A (BPA), and five homologues of ethoxylated bisphenol A dimethacrylate (BisEMA EO2-6) in unstimulated and artificial saliva, and compared their concentrations in the two saliva media following either spiking with a mixture of the compounds or incubation of test specimens of printed biomaterials. Test specimens were immersed in unstimulated/artificial saliva, incubated at 37 °C for 24 h, and saliva aliquots were extracted with methanol and subsequently analyzed by LC-MS/MS.

Preparation of a fluorinated dental resin system and its anti-adhesive properties against S. mutans.

Objectives: The purpose of this study was to characterize physicochemical properties and investigate anti-bacterial adhesion effect of dental resins containing fluorinated monomers.

Method: Fluorinated dimethacrylate FDMA was mixed with commonly used reactive diluent triethylene- glycol dimethacrylate (TEGDMA) and fluorinated diluent 1 H,1 H-heptafluorobutyl methacrylate (FBMA) separately at a mass ratio of 60 wt./40 wt.

Investigation on the antimicrobial activity of chitosan-modified zinc oxide-eugenol cement.

Coronal leakage and reinfection after root canal therapy is an important reason for endodontic failure. Zinc oxide-eugenol (ZOE) -based materials are often used as a coronal seal to prevent secondary infection. The antibacterial effect of ZOE cement is mainly due to leaching of eugenol from the material, but the effect is reported to decrease over time.

Bond strength between dentine and a novel fast-setting calcium silicate cement with fluoride.

The aim of this study was to evaluate the dentine bond strength of a novel fast-setting calcium silicate cement (Protooth) versus a calcium hydroxide-based cement (Dycal), a calcium silicate cement (ProRoot MTA), and a glass ionomer cement (Ketac-Molar). Mid-root dentine slices of 1 mm thickness were obtained from human maxillary incisors. After enlarging the lumen of the canal to 1.