Stability-improved organic n-channel thin-film transistors with nm-thin hydrophobic polymer-coated high-k dielectrics.

We report on the fabrication of N,N'-ditridecyl-perylene-3,4:9,10-tetracarboxylic diimide-C13 (PTCDI-C13), n-channel organic thin-film transistors (OTFTs) with 30 nm Al(2)O(3) whose surface has been un-modified or modified with hexamethyldisilazane (HMDS) and thin hydrophobic CYTOP. Among all the devices, the OTFTs with CYTOP-modified dielectrics exhibit the most superior device performance and stability. The optimum post-annealing temperature for organic n-channels on CYTOP was also found to be as low as 80 °C, although the post-annealing was previously implemented at 120-140 °C for PTCDI domain growth in general.