The Effect of Cooling Conditions on Martensite Transformation Temperature and Hardness of 15% Cr Chromium Cast Iron.

The research reported in the paper concerned the conditions of cooling high-chromium cast iron with about 15% Cr content capable to ensure completeness of transformation of supercooled austenite into martensite in order to obtain high hardness value of the material and thus its high resistance to abrasive wear. For testing, castings were prepared with dimensions 120 mm × 100 mm × 15 mm cast in sand molds in which one of cavity surfaces was reproduced with chills. From the castings, specimens for dilatometric tests were taken with dimensions 4 mm × 4 mm × 16 mm and plates with dimensions 50 mm × 50 mm × 15 mm for heat treatment tests.